| About |
|---|
| ALCOM® LG PC 1000 UV 14094 CC1323-08 is a Polycarbonate (PC) product filled with filler. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Applications of ALCOM® LG PC 1000 UV 14094 CC1323-08 include automotive and lighting applications. Characteristics include: Flame Rated RoHS Compliant Antioxidant High Flow UV Stabilized&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Clarity,High liquidity,Inoxidizability |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 28.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2310 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 65.0 | MPa | |
| — | 65.0 | MPa | |
| Tensile strain | |||
| yield | 6.0 | % | |
| fracture | 24 | % | |
| Bending modulus | 2480 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 78.0 | MPa | |
| — | 102 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| — | 5.0 | kJ/m² | |
| -40℃ | 5.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| — | 88 | kJ/m² | |
| -40℃ | 75 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 141 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | ||
| 0.75 mm | V-2 | ||
| Glowing wire flammability index | |||
| 2.0 mm | 850 | ℃ | |
| 3.0 mm | 850 | ℃ | |
| 4.0 mm | 850 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| Total, 1000 µ m | 88.5 | % | |
| Total, 2000 µ m | 85.5 | % | |
| Total, 3000 µ m | 81.5 | % | |
| Total, 4000 µ m | 76.0 | % | |
| Haze | |||
| 1000 µm | 94 | % | |
| 2000 µm | 95 | % | |
| 3000 µm | 95 | % | |
| 4000 µm | 95 | % | |
| Half Power Angle | |||
| 1.00 mm | 12.0 | ° | |
| 2.00 mm | 20.0 | ° | |
| 3.00 mm | 24.0 | ° | |
| 4.00 mm | 28.0 | ° |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 100 to 120 | °C | |
| Drying time – hot air dryer | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Processing (melt) temperature | 270 to 310 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. A, 2° |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |