| ALCOM® PC 740/4 WT1281-10LD是一种聚碳酸酯（PC）产品,含有的填充物为填料。 它,在北美洲、欧洲或亚太地区有供货。 ALCOM® PC 740/4 WT1281-10LD的应用领域包括汽车行业 和 照明设备。 特性包括: 阻燃/额定火焰 符合 REACH 标准 通过 ROHS 认证 高流动性&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,HB,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 20.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2450 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 66.0 | MPa | ISO 527-2 |
| — | 66.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 6.0 | % | ISO 527-2 |
| fracture | 70 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| 3.50% strain | 76.0 | MPa | ISO 178 |
| — | 100 | MPa | ISO 178 |
| Bending strain | 7.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 11 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 124 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 142 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 0.75 mm | V-2 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.0 mm | 850 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 850 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 850 | ℃ | IEC 60695-2-12 |
| 4.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Fire resistance performance | |||
| 1.00 mm | passed | FMVSS |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| Total, 1000 µ m | 26.0 | % | ISO 13468 |
| Haze | |||
| 1000 µm | 94 | % | ISO 13468 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Half Power Angle（T，Y） | 59.0 | ° |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 100 to 120 | °C | |
| Hot air dryer | 100 to 120 | °C | |
| Drying time | |||
| Desiccant desiccant | 4.0 to 12 | hr | |
| Hot air dryer | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 270 to 310 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |