| ALCOM® PC + AWL 750/20.1 WT1407-04LB是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)产品,含有的填充物为20% 填料。 它,在北美洲、欧洲或亚太地区有供货。 ALCOM® PC + AWL 750/20.1 WT1407-04LB的应用领域包括电气/电子应用、反射镜、汽车行业 和 照明设备。 特性包括: 符合 REACH 标准 通过 ROHS 认证&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High reflectivity |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 20.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 80 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 120 | ℃ | ISO 306 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 91 | % | DIN 5033 |
| Y10 of Transmittance：500.0 µm | 0.10 | % | ISO 13468 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 118 | MPa | ISO 2039-1 |
| Tensile modulus | 2800 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 53.0 | MPa | |
| fracture | 50.0 | MPa | |
| Tensile strain | ISO 527-2 | ||
| yield | 4.0 | % | |
| fracture | 10 | % | |
| Bending modulus | 2800 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 100 to 110 | °C | |
| Hot air dryer | 100 to 110 | °C | |
| Drying time | |||
| Desiccant desiccant | 4.0 to 8.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 220 to 280 | °C | |
| Mold temperature | 70.0 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |