| Alcryn® 2170 NC是一种熔融加工性橡胶(MPR)材料,。 该产品在亚太地区、北美洲或欧洲有供货,。 Alcryn® 2170 NC的主要特性有: 符合 WEEE 标准 通过 ROHS 认证 耐化学品 耐磨 良好的抗撕裂强度 典型应用领域包括: 电线电缆 软管 密封应用 工程/工业配件 手柄&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | MPR |
| Material Status | Commercial: Active |
| Features | High Friction,High liquidity,Good tear strength,Good wear resistance,Solvent resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Density | 1.21 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 1.90 mm | 12.4 | MPa | ISO 37 |
| Fracture, 1.90 mm | 12.4 | MPa | ASTM D412 |
| 100% strain | 2.80 | MPa | ASTM D412 |
| 100% strain, 1.90 mm | 2.80 | MPa | ISO 37 |
| Tensile strain | |||
| Fracture, 1.90 mm | 600 | % | ISO 37 |
| fracture | 600 | % | ASTM D412 |
| tear strength | |||
| 24℃ | 56.0 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395 | ||
| 24℃，22 hr | 18 | % | ASTM D395 |
| 100℃，22 hr | 88 | % | ASTM D395 |
| Compression deformation | ISO 815 | ||
| 24℃，22 hr | 18 | % | ISO 815 |
| 100℃，22 hr | 88 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw A, 1.90 mm, molded | 68 | ASTM D2240 | |
| Shaw A, 1.90 mm, molded | 68 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -60.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -60.0 | ℃ | ISO 812 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |