| Alcryn® 2360 NC is a Melt Processable Rubber (MPR) product. It is available in Asia Pacific, Europe, or North America. Characteristics include: RoHS Compliant WEEE Compliant&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | MPR |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shaw’s A | 61 | ASTM D2240 | |
| Shaw’s A | 61 | ISO 868 | |
| Taber abraser | ASTM D1044 | ||
| 1000 g, CS-17 wheel | 0.0310 | mg | ASTM D1044 |
| 1000 g, CS-18 wheel | 0.333 | mg | ASTM D1044 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile permanent deformation | 9 | % | ASTM D412 |
| tensile strength | |||
| yield | 8.27 | MPa | ISO 37 |
| yield | 8.27 | MPa | ASTM D412 |
| 100% strain | 2.55 | MPa | ASTM D412 |
| 100% strain | 2.55 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 380 | % | ASTM D412 |
| fracture | 380 | % | ISO 37 |
| tear strength | |||
| 24℃ | 25 | kN/m | ISO 34-1 |
| 24℃ | 24.5 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395A | ||
| 24℃，22 hr | 16 | % | ASTM D395A |
| 70℃，22 hr | 52 | % | ASTM D395A |
| 100℃，22 hr | 66 | % | ASTM D395A |
| Compression deformation | ISO 815 | ||
| 24℃，22 hr | 16 | % | ISO 815 |
| 70℃，22 hr | 52 | % | ISO 815 |
| 100℃，22 hr | 66 | % | ISO 815 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -41.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -41.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | ASTM D573 | ||
| 125℃，168 hr | 130 | % | ASTM D573 |
| 100% Strain，125℃，168 hr | 110 | % | ASTM D573 |
| The rate of change in tensile strength in air | ISO 188 | ||
| 125℃，168 hr | 130 | % | ISO 188 |
| 100% strain 125 ℃, 168 hr | 110 | % | ISO 188 |
| The rate of change in ultimate elongation in air | |||
| 125℃，168 hr | 96 | % | ASTM D573 |
| Change in Tensile Strain at Break in Air（125℃，168 hr） | 96 | % | ISO 188 |
| Volume change | ASTM D471 | ||
| 100℃，168 hr，in ASTM #1 Oil | -28 | % | ASTM D471 |
| 100℃，168 hr，in IRM 903 Oil #3 | -19 | % | ASTM D471 |
| 100 ℃, 168 hr, in water | -43 | % | ASTM D471 |
| Volume change | ISO 1817 | ||
| 100℃，168 hr，in ASTM #1 Oil | -28 | % | ISO 1817 |
| 100 ℃, 168 hr, in water | -43 | % | ISO 1817 |
| 100℃，56640 hr，in IRM 903 Oil #3 | -19 | % | ISO 1817 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ASTM D792 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Apparent Viscosity（190℃，300 sec^-1） | 170 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 177 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |