| Alcryn® 4060 NC是一种熔融加工性橡胶(MPR)材料,。 该产品在北美洲、欧洲或亚太地区有供货,加工方式为:吹塑成型、挤出、压延或真空成型。 Alcryn® 4060 NC的主要特性有: 通过 ROHS 认证 环保/绿色 快速成型周期 耐化学品 耐热 典型应用领域包括: 电线电缆 工程/工业配件 软管 手柄 涂覆应用&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | MPR |
| Material Status | Commercial: Active |
| Features | Renewable resources,noise reduction,Quick molding cycle,High Heat Resistance,Moderate liquidity,Grease resistance,Ozone resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shaw A, 1.90 mm, molded | 57 | ISO 868 | |
| Shaw A, 1.90 mm, molded | 57 | ASTM D2240 | |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 4.00 | mg | ASTM D1044 |
| Torsional modulus | ASTM D1043 | ||
| -20℃，1.90 mm | 6.80 | MPa | ASTM D1043 |
| 24℃，1.90 mm | 1.70 | MPa | ASTM D1043 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile permanent deformation | 7 | % | ASTM D412 |
| tensile strength | |||
| Yield, 1.90 mm | 8.40 | MPa | ASTM D412 |
| Yield, 125 ℃, 1.90 mm | 8.20 | MPa | ASTM D573 |
| Tensile strain | |||
| Fracture, 1.90 mm | 440 | % | ISO 37 |
| Fracture, 125 ℃, 1.90 mm | 400 | % | ISO 188 |
| tear strength | |||
| 1.90 mm | 29.7 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 24℃，22 hr | 16 | % | ASTM D395B |
| 100℃，22 hr | 72 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 24℃，22 hr | 16 | % | ISO 815 |
| 100℃，22 hr | 72 | % | ISO 815 |
| Kappa’s modulus | |||
| -40℃ | 68.9 | MPa | ASTM D1043 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -69.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -69.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Change in Durometer Hardness in Air (125 ℃, 168 hr) | -3.0 | ASTM D573 | |
| The rate of change of Shore hardness in air | |||
| Shaw A, 125 ℃, 168 hr | -3.0 | ISO 188 | |
| Volume change | ASTM D471 | ||
| 27℃，168 hr，in Reference Fuel B | 13 | % | ASTM D471 |
| 100℃，168 hr，in ASTM #1 Oil | -19 | % | ASTM D471 |
| 100℃，168 hr，in IRM 903 Oil | 14 | % | ASTM D471 |
| 100 ℃, 168 hr, in water | 9.0 | % | ASTM D471 |
| Volume change | ISO 1817 | ||
| 27℃，168 hr，in Reference Fuel B | 13 | % | ISO 1817 |
| 100℃，168 hr，in ASTM #1 Oil | -19 | % | ISO 1817 |
| 100℃，168 hr，in IRM 903 Oil | 14 | % | ISO 1817 |
| 100 ℃, 168 hr, in water | 9.0 | % | ISO 1817 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ASTM D471 |
| Density | 1.17 | g/cm³ | ISO 2781 |
| Apparent viscosity of melt | |||
| 190℃，300 sec^-1 | 400 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 166 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |