About
EVA resin ALCUDIA® PA-420-L features low gel content and is recommended for extrusion coating applications, especially when high productions speeds are required. PA-420-L is also particularly suitable for co-extrusion with other polymers. It contains antioxidant and free flowing agent. TYPICAL APPLICATIONS Extrusion coating Thermal adhesive layer in lamination (e.g. graphic arts) Co-extrusion Packaging films PA-420-L is designed to be processed at temperatures as high as 220°C in high speed extrusion coating lines. Processing conditions should be optimised for each production line.&&

About

EVA resin ALCUDIA® PA-420-L features low gel content and is recommended for extrusion coating applications, especially when high productions speeds are required. PA-420-L is also particularly suitable for co-extrusion with other polymers. It contains antioxidant and free flowing agent. TYPICAL APPLICATIONS Extrusion coating Thermal adhesive layer in lamination (e.g. graphic arts) Co-extrusion Packaging films PA-420-L is designed to be processed at temperatures as high as 220°C in high speed extrusion coating lines. Processing conditions should be optimised for each production line.&&

Product Description
Supplier	REPSOL
Generic	EVA
Material Status	Commercial: Active
Features	Low speed solidification point,Food contact compliance,Inoxidizability
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.940	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	20	g/10min	ISO 1133
Vinyl acetate content	20.0	wt%

MECHANICAL	Nominal value	Unit	Test method
Shore hardness			ISO 868
Shaw’s A	84		ISO 868
Shaw’s D	30		ISO 868
tensile strength
fracture	11.0	MPa	ISO 527-2
Tensile strain
fracture	780	%	ISO 527-2

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	53.0	℃	ISO 306/A
Melting temperature	82.0	℃

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	220	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.