| About |
|---|
| EVA resin ALCUDIA® PA-461 is recommended for hot melt adhesives applications, when toughness and flexibility are required. It contains antioxidant and free flowing agent. TYPICAL APPLICATIONS Hot Melt Adhesives Packaging Bookbinding Pressure sensitive adhesive coatings Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line.&& |
| Product Description | |
|---|---|
| Supplier | REPSOL |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Food contact compliance,Inoxidizability |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Melting temperature | 59.0 | ℃ | |
| Ring and Ball Softening Point | 112 | ℃ | ASTM E28 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 73 | ISO 868 | |
| tensile strength | |||
| fracture | 5.00 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 850 | % | ISO 527-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 45 | g/10min | ISO 1133 |
| Vinyl acetate content | 33.0 | wt% | |
| Brookfield viscosity | Internal Method | ||
| 180℃ | 293 | Pa·s | Internal Method |
| 200℃ | 169 | Pa·s | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Spindle SC4-27 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |