ALCUDIA® HDPE 5606-T

About
The high density polyethylene ALCUDIA® 5606T is a homopolymer of medium molecular weight. Due to its good processability characteristics is specially intended for extrusion of doubled corrugated drainage and sewage pipes. This product is supplied in natural colour but they can be easily coloured with pigments steady at processing temperature, using dry-colouring or masterbatch techniques. TYPICAL APPLICATIONS Structured doubled wall without pressure pipes for underground drainage and sewage. Mono and doubled wall corrugated pipes for protecting cables. Recommended melt temperature range 190 – 210 °C. Processing conditions should be optimised for each production line.&&

About

The high density polyethylene ALCUDIA® 5606T is a homopolymer of medium molecular weight. Due to its good processability characteristics is specially intended for extrusion of doubled corrugated drainage and sewage pipes. This product is supplied in natural colour but they can be easily coloured with pigments steady at processing temperature, using dry-colouring or masterbatch techniques. TYPICAL APPLICATIONS Structured doubled wall without pressure pipes for underground drainage and sewage. Mono and doubled wall corrugated pipes for protecting cables. Recommended melt temperature range 190 – 210 °C. Processing conditions should be optimised for each production line.&&

Product Description
Supplier	REPSOL
Generic	MMW-HDPE
Material Status	Commercial: Active
Features	Excellent Processability,Food contact compliance,Hexene copolymers,Good coloring
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.956	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.60	g/10min	ISO 1133
190℃，21.6kg	40	g/10min	ISO 1133
190℃，5.0kg	2.0	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, F50	> 15.0	hr	ASTM D1693

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	28.0	MPa	EN 638
Tensile strain
fracture	700	%	EN 638
Bending modulus	1400	MPa	ASTM D790

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -70.0	℃	ASTM D746

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	190 to 210	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.