| About |
|---|
| Alkathene LDJ225 is a low density polyethylene designed for use in the production of low gauge (20 – 50µm), high quality film. Alkathene LDJ225 is formulated with a process stabilisation and antiblock additive package and contains other additives designed to confer very high levels of slip. Film Extrusion: Alkathene LDJ225 is intended primarily for use in bread bag film and other low gauge applications requiring very high slip. It is typically blended with LLDPE for applications such as lamination and overwrap films.&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Smoothness,High anti-blocking,Low density |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.5 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 32 | µm | |
| Secant modulus | |||
| 2% secant, MD: 32 µ m | 160 | MPa | |
| 2% secant, TD: 32 µ m | 190 | MPa | |
| tensile strength | |||
| MD, yield, 32 µ m | 11.0 | MPa | |
| TD, yield, 32 µ m | 10.0 | MPa | |
| MD, fracture, 32 µ m | 23.0 | MPa | |
| TD, fracture, 32 µ m | 16.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 32 µ m | 290 | % | |
| TD, fracture, 32 µ m | 720 | % | |
| Drop hammer impact | |||
| 32 µm | 70 | g | ASTM D1709 |
| tear strength | |||
| MD，32 µm | 4 | N | |
| TD，32 µm | 2 | N |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，32 µm | 69 | ASTM D2457 | |
| Haze | |||
| 32 µm | 8.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.79 in/min |
| 3. 20 in/min |
| 4. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |