| Alkathene LDJ226 is a low density polyethylene designed for a variety of low gauge (20-50µm) general purpose applications where antistatic or a low to medium slip film is required. Alkathene LDJ226 is formulated with a process stabilisation and antiblock package and contains an antistatic additive. Film Extrusion: Alkathene LDJ226 is intended for use in a wide range of shrink and other low gauge film applications including carry bags and overwrap films that require antiblock and a low to medium level of slip.&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High anti-blocking,Low density,Antistatic property |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.5 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 32 | µm | |
| Secant modulus | |||
| 2% secant, MD: 32 µ m | 160 | MPa | |
| 2% secant, TD: 32 µ m | 190 | MPa | |
| tensile strength | |||
| MD, yield, 32 µ m | 11.0 | MPa | |
| TD, yield, 32 µ m | 10.0 | MPa | |
| MD, fracture, 32 µ m | 22.0 | MPa | |
| TD, fracture, 32 µ m | 16.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 32 µ m | 270 | % | |
| TD, fracture, 32 µ m | 740 | % | |
| Drop hammer impact | |||
| 32 µm | 70 | g | ASTM D1709 |
| tear strength | |||
| MD，32 µm | 4 | N | |
| TD，32 µm | 2 | N |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，32 µm | 71 | ASTM D2457 | |
| Haze | |||
| 32 µm | 7.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.79 in/min |
| 3. 20 in/min |
| 4. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |