| Alloy Exchange Reprocessed ABS001 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in North America. Primary attribute of Alloy Exchange Reprocessed ABS001: Eco-Friendly/Green. Typical application of Alloy Exchange Reprocessed ABS001: Automotive&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792-A |
| Melt Flow Rate | |||
| 230℃，3.80kg | 5.2 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 3.24 mm | 47.3 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.24 mm | 19 | % | ASTM D638 |
| Bending modulus | |||
| Tangent, 3.24 mm | 2580 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 85.2 | ℃ | ASTM D648-A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. No. of specimens tested: 3 |
| 3. Procedure A |
| 4. No. of specimens tested: 2 Samples dried 8 hours at 90°C. |
| 5. Type I, 2.0 in/min |
| 6. No. of specimens tested: 5 |
| 7. Method I (3 point load) |
| 8. No. of specimens tested: 2 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |