| About |
|---|
| lphalac of LG chemical is high functionality styrene resin and offers excellent properties and processibility .This product can be accepted as the replacement of general ABS resins.&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,High impact resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 200℃，5.0kg | 3.7 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 40 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 10 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 82.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 34.3 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 38 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2230 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 52.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Barrel rear temperature | 170 to 190 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Processing (melt) temperature | 190 to 220 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |