| About |
|---|
| ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP is a Polypropylene Homopolymer (PP Homopolymer) product filled with 10% glass bead and 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include: Flame Rated RoHS Compliant Chemically Coupled Heat Stabilizer High Stiffness&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low odor,Chemical coupling,Heat Stabilized,Homopolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：24 hrs | 0.50 to 0.80 | % | |
| MD：24 hrs | 0.30 to 0.60 | % | |
| Spiral flow length | |||
| 1.00 mm | 30.0 | n | |
| 2.00 mm | 85.0 | n | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5300 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 70.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | 4500 | MPa | ISO 178 |
| bending strength | 105 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| — | 5.0 | kJ/m² | |
| -40℃ | 4.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| — | 31 | kJ/m² | |
| -40℃ | 14 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 147 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 130 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 166 | ℃ | ISO 11357 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Processing (melt) temperature | 200 to 270 | °C | |
| Mold temperature | 20 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |