| ALTECH® PA6 A 2045/100 GF45是一种聚酰胺6（尼龙6）产品,含有的填充物为45% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在亚太地区、北美洲或欧洲有供货。 典型应用领域为:工程/工业配件。 特性包括: 阻燃/额定火焰 符合 REACH 标准 通过 ROHS 认证 优良的脱模剂 热稳定剂&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good stripping performance,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ISO 1183 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 6.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 15000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 190 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.9 | % | ISO 527-2 |
| Bending modulus | 12000 | MPa | ISO 178 |
| bending strength | 275 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 70 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 200 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 450 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 12 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |