| About |
|---|
| ALTECH® PA6 A 3030/109 GB30 NC0001-00 is a Polyamide 6 (Nylon 6) product filled with 30% glass bead. It can be processed by gas-assisted injection molding and is available in Asia Pacific, Europe, or North America. Applications of ALTECH® PA6 A 3030/109 GB30 NC0001-00 include engineering/industrial parts and housings. Characteristics include: Flame Rated RoHS Compliant Good Mold Release Heat Stabilizer High Flow&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low warping,High liquidity,Good stripping performance,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Relative viscosity | 3.20 | ISO 307 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4300 | MPa | ISO 527-2 |
| tensile strength | 70.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 4.0 | % | ISO 527-2 |
| Bending modulus | 3600 | MPa | ISO 178 |
| bending strength | 110 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| — | 4.0 | kJ/m² | |
| -40℃ | 2.5 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| — | 50 | kJ/m² | |
| -40℃ | 33 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 78.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 203 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 11357 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 12 | hr | |
| Recommended maximum moisture content | < 0.15 | % | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. m-Cresol,c = 10 g/l |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |