| About |
|---|
| ALTECH® PA6 A 4230/140 MR20 GF10 FR是一种聚酰胺6（尼龙6）产品,含有的填充物为10% 玻璃纤维增强材料 和 20% 矿物填料。 它可以通过注射成型进行加工,在北美洲、欧洲或亚太地区有供货。 ALTECH® PA6 A 4230/140 MR20 GF10 FR的应用领域包括电气/电子应用 和 房屋。 特性包括: 阻燃/额定火焰 符合 REACH 标准 通过 ROHS 认证 Flame Retardant 低收缩性&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low contractility,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 20.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.70 | % | ISO 294-4 |
| MD：24 hrs | 0.40 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7300 | MPa | ISO 527-2 |
| tensile strength | 80.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | 6300 | MPa | ISO 178 |
| bending strength | 125 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 30 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 195 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 208 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 12 | hr | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |