| About |
|---|
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Material Status | Commercial: Negative |
| Features | weathering resistance,Good Clarity,High Flexibility |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water absorption rate | 0.4 | % | ISO 62 |
| Mold shrinkage rate | 0.2-0.6 | ASTM D-955 | |
| Melt Flow Rate | |||
| 230℃，3.8kg | 2 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat softening point temperature | 117 | ℃ | ISO 306B50 |
| Hot deformation temperature | |||
| 1.8MPa | 110 | ℃ | ISO 75-2 |
| Linear coefficient of thermal expansion | 65 | 10-°K | ASTM D-696 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.49 | ISO R-489 | |
| Transmittance | 92 | % | ASTM D-1003 |
| Haze | 0.5 | % | ASTM D-1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 70 | MPa | ISO 527-2 |
| elongation at break | 5 | % | ISO 527-2 |
| Bending modulus | 3450 | MPa | ISO 178 |
| Rockwell hardness | M-102 | ASTM D-785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 20 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | 2 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | 2 | J/m | ISO 180/1A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardancy | HB | class | UL94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |