| About |
|---|
| Altuglas® SG10 is a Polymethyl Methacrylate Acrylic product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 4.5 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.36 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/2U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 90.0 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD：-30~23℃ | 1.0E-4 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 15 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 3.90 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.040 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ISO 489 | |
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 37 | ASTM D785 | |
| tensile strength | |||
| Fracture, 23 ℃ | 37.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 30 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1700 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 60.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 75 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 225 to 245 | °C | |
| Mold temperature | 60 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |