| About |
|---|
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.19 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，50%HR，24h | 0.3 | % | ASTM D570 |
| Mold shrinkage rate | 0.2-0.6 | % | ASTM D955 |
| Melt Flow Rate | |||
| 230℃，3.8kg | 3.7 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress | |||
| Maximum, 23 ℃ | 70 | MPa | ASTM D638 |
| elongation at break | |||
| 23℃ | 6 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 3100 | MPa | ASTM D790 |
| Bending stress | |||
| Maximum, 23 ℃ | 103 | MPa | ASTM D790 |
| surface hardness | |||
| 23℃ | 93 | HRM | ASTM D785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 1.2 | KJ/m² | ASTM D256 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | |||
| 23°C –Method A | 1.49 | ASTM D542 | |
| Transmittance | |||
| 23℃，3.2mm | 92 | % | ASTM D1003 |
| Haze | |||
| 23℃，3.2mm | ＜1 | % | ASTM D1003 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| vicat softening point | |||
| 50°C/hr，1kg | 111 | ℃ | ASTM D1525 |
| 104 | ℃ | ASTM D1525 | |
| Hot deformation temperature | |||
| 18.6kgf/cm2 | 102 | ℃ | ASTM D648 |
| Under load, annealed at 4.6kgf/cm2 | 105 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.2mm | HB | calss | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |