| About |
|---|
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.8Kg | 2.8 | g/10min | ISO 1133 |
| Molding shrinkage | |||
| Flowing flow | 0.2-0.6 | % | ASTM D955 |
| Water Absorption | |||
| Equilibrium, 23 ℃, 50% r. h | 0.3 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength | |||
| Break | 70 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Break | 5 | % | ISO 527-2 |
| Flexural Modulus | 3300 | MPa | ISO 178 |
| Rockwell hardness | 97 | ASTM D-785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 2.0 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, Annealed | 100 | ℃ | ISO 75-2/A |
| Vicat Softening Temperature | 108 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion CLTE | |||
| Flowing flow | 6.5E-5 | cm/cm/℃ | ASTM D696 |
| Specific Heat | 2090 | J/kg/℃ | ASTM C351 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive Index | 1.49 | % | ISO 489 |
| Light Transmittance | 93 | % | ASTM D1003 |
| Haze | <1.00 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Drying Temperature | 85-90 | ℃ | |
| Drying Time | 4.0-6.0 | hr | |
| Rear Temperature | 220-240 | ℃ | |
| Middle Temperature | 230-250 | ℃ | |
| Front Temperature | 240-260 | ℃ | |
| Nozzle temperature | 240-260 | ℃ | |
| Processing (Melt) Temperature | 240-260 | ℃ | |
| Mold Temperature | 80-85 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |