| Americas Styrenics EB6755是一种高抗冲聚苯乙烯材料,。 该产品在北美洲有供货,加工方式为:注射成型、挤出或热成型。 Americas Styrenics EB6755的主要特性有: 可接触食品 高抗环境应力断裂能力 (ESCR) 耐冲击 良好的韧性 典型应用领域包括: 包装 容器 食品接触应用 帽子/盖子/瓶塞&& |
| Product Description | |
|---|---|
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good flexibility,Food contact compliance,low-temperature impact resistance,High ESCR |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.2 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：24 hrs | 0.40 to 0.80 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23 ℃, molded | 110 | J/m | ASTM D256 |
| 23 ℃, injection molding | 140 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 89.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 79.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 93 | ASTM D785 | |
| Tensile modulus | |||
| injection molding | 1400 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Fracture, injection molding | 22.7 | MPa | ASTM D638 |
| injection molding | 22.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, injection molding | 75 | % | ASTM D638 |
| Bending modulus | |||
| injection molding | 1400 | MPa | ASTM D790 |
| bending strength | |||
| injection molding | 28.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel rear temperature | 218 to 249 | °C | |
| Barrel middle temperature | 218 to 249 | °C | |
| Barrel front temperature | 199 to 213 | °C | |
| Nozzle temperature | 213 to 243 | °C | |
| Mold temperature | 16 to 66 | °C | |
| Barrel 1 zone temperature | 177 to 193 | °C | |
| Barrel 2 zone temperature | 182 to 204 | °C | |
| Barrel 3 zone temperature | 188 to 210 | °C | |
| Barrel 4 zone temperature | 199 to 216 | °C | |
| Barrel 5 zone temperature | 204 to 221 | °C | |
| Connector temperature | 193 to 232 | °C | |
| Melt temperature | 193 to 232 | °C | |
| Nozzle temperature | 199 to 232 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |