Amodel® A-4160 L

About
Amodel® A-4160 L is a 60% glass reinforced polyphthalamide (PPA) which exhibits high modulus, a high heat deflection temperature, and exceptional creep resistance. This material was designed to replace metal and is particularly suited for corrosion sensitive applications. Its rapid crystallization and good flow characteristics allow shorter cycles for enhanced molding productivity. Black: A-4160 L BK324&&

About

Amodel® A-4160 L is a 60% glass reinforced polyphthalamide (PPA) which exhibits high modulus, a high heat deflection temperature, and exceptional creep resistance. This material was designed to replace metal and is particularly suited for corrosion sensitive applications. Its rapid crystallization and good flow characteristics allow shorter cycles for enhanced molding productivity. Black: A-4160 L BK324&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Negative
Features	Good Rigidity,Low CLTE,Good flexibility,Good Dimensional Stability,Quick molding cycle,Non-corrosiveness,Lubricating,Solvent resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.75	g/cm³	ISO 1183/A
Shrinkage rate			ISO 294-4
TD	0.80	%	ISO 294-4
MD	0.50	%	ISO 294-4
Water absorption rate
23℃，24hr	0.19	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	23300	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	244	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	1.4	%	ISO 527-2
Bending modulus
23℃	19300	MPa	ISO 178
bending strength
23℃	385	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	13	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	130	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	304	℃	ISO 75-2/A

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0	hr
Barrel rear temperature	318 to 324	°C
Barrel front temperature	327 to 332	°C
Processing (melt) temperature	329 to 343	°C
Mold temperature	66 to 93	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.