Amodel® A-6135 HN

About
Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, non-lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Black: A-6135 HN BK 324&&

About

Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, non-lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Black: A-6135 HN BK 324&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good liquidity,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.45	g/cm³	ISO 1183/A
Shrinkage rate			ISO 294-4
TD	0.90	%	ASTM D955
MD	0.60	%	ASTM D955
TD	1.0	%	ISO 294-4
MD	0.50	%	ISO 294-4
Water absorption rate
24hr	0.30	%	ASTM D570
23℃，24hr	0.29	%	ISO 62

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	9.2	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	60	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch	85	J/m	ASTM D256
23℃	9.1	kJ/m²	ISO 180
Impact strength of cantilever beam notch	800	J/m	ASTM D256
Notched impact strength of cantilever beam
23℃	62	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed, 3.2 mm	291	℃	ASTM D648
1.8 MPa, unannealed	288	℃	ISO 75-2/A
0.45 MPa, unannealed	303	℃	ISO 75-2/B
Melting temperature	310	℃	ISO 11357-3
Melting temperature	310	℃	ASTM D570
Linear coefficient of thermal expansion
TD			ASTM E831
MD			ASTM E831
0 to 100 ℃	2.2E-5	cm/cm/℃	ASTM E831
100 to 200 ℃	1.6E-5	cm/cm/℃	ASTM E831
0 to 100 ℃	6.1E-5	cm/cm/℃	ASTM E831
100 to 200 ℃	1.0E-4	cm/cm/℃	ASTM E831

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	13800	MPa	ASTM D638
Tensile modulus			ISO 527-2
23℃	11500	MPa	ISO 527-2
100℃	7310	MPa	ISO 527-2
150℃	6270	MPa	ISO 527-2
175℃	5310	MPa	ISO 527-2
tensile strength	203	MPa	ASTM D638
tensile strength			ISO 527-2
Fracture, 23 ℃	211	MPa	ISO 527-2
Fracture, 24 ℃	121	MPa	ISO 527-2
Fracture, 150 ℃	92.4	MPa	ISO 527-2
Fracture, 175 ℃	82.0	MPa	ISO 527-2
Tensile strain			ISO 527-2
fracture	1.9	%	ASTM D638
Fracture, 23 ℃	2.0	%	ISO 527-2
Fracture, 24 ℃	4.3	%	ISO 527-2
Fracture, 150 ℃	4.9	%	ISO 527-2
Fracture, 175 ℃	4.7	%	ISO 527-2
Bending modulus	11400	MPa	ASTM D790
Bending modulus			ISO 178
23℃	11400	MPa	ISO 178
100℃	6600	MPa	ISO 178
150℃	4900	MPa	ISO 178
175℃	4600	MPa	ISO 178
bending strength	310	MPa	ASTM D790
bending strength			ISO 178
3.50% strain, 23 ℃	300	MPa	ISO 178
3.50% strain, 100 ℃	170	MPa	ISO 178
3.50% strain, 150 ℃	123	MPa	ISO 178
3.50% strain, 175 ℃	112	MPa	ISO 178
compressive strength	148	MPa	ASTM D695
shear strength	87.6	MPa	ASTM D732
Poisson’s ratio	0.39		ASTM E132
Rockwell hardness
R-level	125		ASTM D785

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.045	%
Barrel rear temperature	316 to 321	°C
Barrel front temperature	327 to 332	°C
Processing (melt) temperature	321 to 335	°C
Mold temperature	66 to 93	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.