Amodel® A-8940 HS

About
Amodel® A-8940 HS is a 40% glass-fiber-reinforced, heat-stabilized polyphthalamide (PPA) with a high heat deflection temperature and very high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Black: A-8940 HS BK 328 Natural: A-8940 HS NT&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Low moisture absorption
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.57	g/cm³	ISO 1183/A
Shrinkage rate
TD	0.68	%	ASTM D955
MD	0.34	%	ASTM D955
Water absorption rate
24hr	0.15	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	15100	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	243	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	2.0	%	ISO 527-2
Bending modulus
23℃	14500	MPa	ISO 178
bending strength
Fracture, 23 ℃	357	MPa	ISO 178
Fracture bending strain
23℃	2.6	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	9.5	kJ/m²	ISO 179/1eA
23℃	9.7	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	59	kJ/m²	ISO 179/1eU
23℃	60	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	10	kJ/m²	ISO 180-A
Notched impact strength of cantilever beam			ISO 180/A
-30℃	55	kJ/m²	ISO 180/A
23℃	59	kJ/m²	ISO 180/A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	293	℃	ISO 75-2/Af
0.45 MPa, unannealed	311	℃	ISO 75-2/Bf
Melting temperature	323	℃	ISO 11357-3

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.030 to 0.060	%
Barrel rear temperature	316 to 329	°C
Barrel middle temperature	316 to 329	°C
Barrel front temperature	324 to 335	°C
Processing (melt) temperature	321 to 343	°C
Mold temperature	170	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.