| About |
|---|
| Amodel® AE-8930 is a 30% glass reinforced polyphthalamide (PPA) designed to work in the modern automotive electrical environment. This grade features a high heat deflection temperature, high flexural modulus and high tensile strength, as well as excellent creep resistance and low moisture absorption. Black: AE-8930 BK938 Natural: AE-8930 NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Ethylene glycol,Good flexibility,Good Dimensional Stability,Non-corrosiveness,High Heat Resistance,Solvent resistance,Low moisture absorption,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 11900 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 210 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.3 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 11000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 300 | MPa | ISO 178 |
| Bending strain | 2.9 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 56 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.2 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 290 | ℃ | ISO 75-2/A |
| Glass transition temperature | 135 | ℃ | DSC |
| Melting temperature | 325 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 4.35 | ASTM D150 | |
| 1 MHz | 4.02 | ASTM D150 | |
| Dissipation factor | |||
| 60 Hz | 7.0E-3 | ASTM D150 | |
| Compared to the leakage tracing index | |||
| 3.00 mm, solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 0.80 mm | 750 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.030 to 0.060 | % | |
| Barrel rear temperature | 316 to 330 | °C | |
| Barrel middle temperature | 316 to 330 | °C | |
| Barrel front temperature | 324 to 340 | °C | |
| Processing (melt) temperature | 330 to 350 | °C | |
| Mold temperature | 150 to 165 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. This value is equivalent to 0.23EE-04 by ISO 11359 |
| 3. This is equivalent to 0.23EE-04 /°K by ISO 11359 |
| 4. This is equivalent to 0.27EE-04 /°K by ISO 11359 |
| 5. This is equivalent to 0.33EE-04 /°K by ISO 11359 |
| 6. This is equivalent to 0.31EE-04 /°K by ISO 11359 |
| 7. This is equivalent to 0.35EE-04 /°K by ISO 11359 |
| 8. Tested at UL |
| 9. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. Tested at UL |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |