| Amodel® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically to be cost effective for most applications requiring high stiffness, good dimensional stability and chemical resistance. Typical applications for Amodel® AS-1566 HS resin include electrical connectors and housings, motor components, pistons, covers, engine parts and transmission components. Black: AS-1566 HS BK 324 Black: AS-1566 HS BK 545 Natural: AS-1566 HS NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low CLTE,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.84 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 0.50 | % | ASTM D955 |
| MD | 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 20000 | MPa | ASTM D638 |
| Tensile modulus | ISO 527-2 | ||
| 23℃ | 22500 | MPa | ISO 527-2 |
| 100℃ | 17200 | MPa | ISO 527-2 |
| 150℃ | 7310 | MPa | ISO 527-2 |
| 175℃ | 6210 | MPa | ISO 527-2 |
| tensile strength | — | MPa | ASTM D638 |
| fracture | 207 | MPa | ASTM D638 |
| tensile strength | ISO 527-2 | ||
| Fracture, 23 ℃ | 200 | MPa | ISO 527-2 |
| Fracture, 24 ℃ | 127 | MPa | ISO 527-2 |
| Fracture, 150 ℃ | 52.4 | MPa | ISO 527-2 |
| Fracture, 175 ℃ | 43.4 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| fracture | 1.7 | % | ASTM D638 |
| Fracture, 23 ℃ | 1.4 | % | ISO 527-2 |
| Fracture, 24 ℃ | 1.5 | % | ISO 527-2 |
| Fracture, 150 ℃ | 3.4 | % | ISO 527-2 |
| Fracture, 175 ℃ | 3.1 | % | ISO 527-2 |
| Bending modulus | 18600 | MPa | ASTM D790 |
| Bending modulus | ISO 178 | ||
| 23℃ | 20500 | MPa | ISO 178 |
| 100℃ | 16800 | MPa | ISO 178 |
| 150℃ | 7310 | MPa | ISO 178 |
| 175℃ | 6410 | MPa | ISO 178 |
| bending strength | — | MPa | ASTM D790 |
| yield | 290 | MPa | ASTM D790 |
| bending strength | ISO 178 | ||
| 23℃ | 284 | MPa | ISO 178 |
| 100℃ | 205 | MPa | ISO 178 |
| 150℃ | 95.8 | MPa | ISO 178 |
| 175℃ | 75.8 | MPa | ISO 178 |
| shear strength | 80.0 | MPa | ASTM D732 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 34 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 64 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 590 | J/m | ASTM D256 |
| 23℃ | 6.5 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 44 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 278 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 280 | ℃ | ISO 75-2/A |
| Melting peak temperature | 311 | ℃ | ASTM D3418 |
| Melting temperature | 311 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | ASTM E831 | ||
| MD | ASTM E831 | ||
| 0 to 100 ℃ | 1.7E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 200 ℃ | 1.7E-5 | cm/cm/℃ | ASTM E831 |
| 0 to 100 ℃ | 4.0E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 200 ℃ | 7.2E-5 | cm/cm/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.045 | % | |
| Hopper temperature | 79 | °C | |
| Barrel rear temperature | 307 to 329 | °C | |
| Barrel front temperature | 307 to 329 | °C | |
| Processing (melt) temperature | 321 to 343 | °C | |
| Mold temperature | > 135 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |