| Amodel® AS-4145 HS polyphthalamide (PPA) is a a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad temperature range, low moisture absorption, excellent chemical resistance and excellent electrical properties. This resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Its rapid crystallization rate and high flow can result in shorter cycles, thereby enhancing molding productivity and lowering costs. Black: AS-4145 HS BK 324&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,Quick molding cycle,High Heat Resistance,Lubricating,Solvent resistance,Low moisture absorption,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 1.0 | % | ASTM D955 |
| MD | 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.21 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 15200 | MPa | ASTM D638 |
| Tensile modulus | 16100 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 224 | MPa | ISO 527-2 |
| fracture | 228 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.2 | % | ISO 527-2 |
| fracture | 2.4 | % | ASTM D638 |
| Bending modulus | 13100 | MPa | ASTM D790 |
| Bending modulus | 13400 | MPa | ISO 178 |
| bending strength | 327 | MPa | ISO 178 |
| yield | 328 | MPa | ASTM D790 |
| compressive strength | 172 | MPa | ASTM D695 |
| shear strength | 89.6 | MPa | ASTM D732 |
| Poisson’s ratio | 0.40 | ASTM E132 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 63 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 100 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 10 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.18 mm | 300 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 298 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed, 3.2 mm | 320 | ℃ | ASTM D648 |
| Continuous use temperature | 210 | ℃ | ASTM D3045 |
| Melting temperature | 320 | ℃ | ISO 11357-3 |
| Melting temperature | 320 | ℃ | ASTM D570 |
| Linear coefficient of thermal expansion | |||
| TD | ASTM E831 | ||
| MD | ASTM E831 | ||
| 0 to 90 ℃ | 1.6E-5 | cm/cm/℃ | ASTM E831 |
| 149 to 249 ℃ | 1.3E-5 | cm/cm/℃ | ASTM E831 |
| 0 to 90 ℃ | 5.9E-5 | cm/cm/℃ | ASTM E831 |
| 149 to 249 ℃ | 1.1E-4 | cm/cm/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 8.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.59 mm | 24 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 4.00 | ASTM D150 | |
| 1 MHz | 3.70 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 4.0E-3 | ASTM D150 | |
| 1 MHz | 0.011 | ASTM D150 | |
| Compared to the leakage tracing index | 600 | V | UL 746 |
| High voltage arc marking rate | |||
| HVTR | 13.0 | mm/min | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Hopper temperature | 79 | °C | |
| Barrel rear temperature | 318 to 324 | °C | |
| Barrel front temperature | 327 to 332 | °C | |
| Processing (melt) temperature | 329 to 343 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1200 hr |
| 3. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |