Amodel® AT-1001L

About
Amodel® AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates. In addition, its chemical and wear resistance, combined with good mechanical properties, make Amodel® AT-1001L resin a prime candidate for applications such as anti-friction and wear resistant components, chemical, oil field, automotive and safety equipment. Natural: AT-1001 L NT&&

About

Amodel® AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates. In addition, its chemical and wear resistance, combined with good mechanical properties, make Amodel® AT-1001L resin a prime candidate for applications such as anti-friction and wear resistant components, chemical, oil field, automotive and safety equipment. Natural: AT-1001 L NT&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Active
Features	Low warping,High impact resistance,Ductility,Lubricating,Good wear resistance,Solvent resistance,low-temperature impact resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.11	g/cm³	ISO 1183/A
Shrinkage rate
TD	1.9 to 2.1	%	ASTM D955
MD	1.7 to 2.2	%	ASTM D955
Water absorption rate
24hr	0.75	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1900	MPa	ASTM D638
tensile strength
fracture	62.1	MPa	ASTM D638
Tensile strain
fracture	30	%	ASTM D638
yield	6.0	%	ASTM D638
Bending modulus	2210	MPa	ASTM D790
bending strength	96.5	MPa	ASTM D790
Poisson’s ratio	0.35		ASTM E132

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-40℃	750	J/m	ASTM D256
23℃	1100	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, annealed, 3.18 mm	120	℃	ASTM D648
Melting temperature	310	℃

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	110	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.045	%
Hopper temperature	79	°C
Barrel rear temperature	304 to 318	°C
Barrel front temperature	316 to 329	°C
Processing (melt) temperature	321 to 343	°C
Mold temperature	66 to 110	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.