| About |
|---|
| Amodel® AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles. Black: AT-6115 HS BK 324 Natural: AT-6115 HS NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Quick molding cycle,Good stripping performance,Lubricating,Good Tensile Strength,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 1.1 | % | ASTM D955 |
| MD | 1.0 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.20 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5380 | MPa | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 5200 | MPa | ISO 527-2 |
| 100℃ | 3100 | MPa | ISO 527-2 |
| tensile strength | 122 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 126 | MPa | ISO 527-2 |
| Fracture, 24 ℃ | 68.3 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.4 | % | ASTM D638 |
| Fracture, 23 ℃ | 4.1 | % | ISO 527-2 |
| Fracture, 24 ℃ | 7.7 | % | ISO 527-2 |
| Bending modulus | 4410 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 4270 | MPa | ISO 178 |
| 100℃ | 2340 | MPa | ISO 178 |
| bending strength | 165 | MPa | ASTM D790 |
| bending strength | ISO 178 | ||
| 23℃ | 170 | MPa | ISO 178 |
| 100℃ | 66.9 | MPa | ISO 178 |
| compressive strength | 100 | MPa | ASTM D695 |
| shear strength | 56.5 | MPa | ASTM D732 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 76 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 55 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 260 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 251 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 298 | ℃ | ISO 75-2/B |
| Melting peak temperature | 305 | ℃ | ASTM D3418 |
| Melting temperature | 305 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD, 0 to 100 ℃ | 2.2E-5 | cm/cm/℃ | ASTM E831 |
| TD, 100 to 200 ℃ | 3.0E-5 | cm/cm/℃ | ASTM E831 |
| MD, 0 to 100 ℃ | 9.0E-5 | cm/cm/℃ | ASTM E831 |
| MD, 100 to 200 ℃ | 1.2E-4 | cm/cm/℃ | ASTM E831 |
| 0 to 100 ℃ | 2.2E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 200 ℃ | 3.0E-5 | cm/cm/℃ | ASTM E831 |
| 0 to 100 ℃ | 9.0E-5 | cm/cm/℃ | ASTM E831 |
| 100 to 200 ℃ | 1.2E-4 | cm/cm/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.045 | % | |
| Barrel rear temperature | 316 to 324 | °C | |
| Barrel front temperature | 327 to 332 | °C | |
| Processing (melt) temperature | 321 to 335 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |