| Amodel AT -6130 HS是30％玻纤增强增韧聚邻苯二甲酰胺（PPA）树脂， 伸长率高于其它30 ％玻纤增强牌号Amodel树脂。专为汽车卡扣式电子连接器开发。流动性好，成型周期短。工艺窗口相对宽泛，模具温度可低至150 °F （65℃ ）。 – 黑色：AT-6130 HS BK 324 -本色： AT-6130 HS NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good liquidity,Low coefficient of friction,High Heat Resistance,Lubricating,Good wear resistance,Solvent resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 0.80 | % | ASTM D955 |
| MD | 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9310 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 170 | MPa | ISO 527-2 |
| fracture | 167 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.3 | % | ISO 527-2 |
| fracture | 3.2 | % | ASTM D638 |
| Bending modulus | 7860 | MPa | ASTM D790 |
| Bending modulus | 7580 | MPa | ISO 178 |
| bending strength | 225 | MPa | ISO 178 |
| yield | 236 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179-1eA |
| Impact strength of cantilever beam notch | 130 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 1400 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 276 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 298 | ℃ | ISO 75-2/B |
| Melting peak temperature | 306 | ℃ | ASTM D3418 |
| Melting temperature | 310 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Barrel rear temperature | 316 to 324 | °C | |
| Barrel front temperature | 327 to 332 | °C | |
| Processing (melt) temperature | 321 to 335 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Injection speed | Fast | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |