| About |
|---|
| AMPLIFY™ GR 205 Functional Polymer is a maleic anhydride grafted (MAH) polymer. The base polymer is a high density polyethylene. Main Characteristics: Maleic anhydride grafted HDPE Polymer compatibilizer Adhesion promoter Promotes adhesion between metal , polyolefins, cellulose, polyester, polycarbonate, glass and foil. Complies with: U.S. FDA 21 CFR 177.1520(c)6 EU, No 10/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | 马来酸酐接枝共聚物 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238，ISO 1133 |
| MAH grafting level | 非常高 | Internal Method | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 129 | ℃ | ASTM D1525 , ISO 306 |
| Melting temperature | |||
| DSC | 130 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 , ISO 868 | ||
| Shaw’s A | 98 | ASTM D2240 , ISO 868 | |
| Shaw’s D | 67 | ASTM D2240 , ISO 868 | |
| tensile strength | |||
| fracture | 15.9 | MPa | ASTM D638 |
| fracture | 15.9 | MPa | ISO 527-2/51 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D638 |
| fracture | 300 | % | ISO 527-2/51 |
| Bending modulus | |||
| 2% secant | 924 | MPa | ASTM D790A , ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Low <0.25 wt %, Medium 0.25-0.5 wt %, High >0.5 wt %, Very High >1.0 wt% |
| 3. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |