| About |
|---|
| MVR (330°C/2.16kg) 18 cm³/10 min; easy release; UV stabilized; ‘softening temperature (VST/B 120)=182°C; injection molding – melt temperature 330 – 340°C; Lamp covers; Headlamp lenses&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good liquidity,Good stripping performance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 330℃，2.16kg | 19 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 330℃，2.16 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 0.85 | % | ISO 294-4 |
| MD：2.0 mm | 0.85 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.30 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.12 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 157 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 172 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B120 | 182 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 6.5E-5 | 1/℃ | ISO 11359-2 |
| MD：23~55℃ | 6.5E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance | 150 | ℃ | UL 746 |
| Strength mechanical performance | 150 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 23 ℃，1 mm | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 23℃，100 Hz | 2.90 | IEC 60250 | |
| 23℃，1 MHz | 2.80 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 23℃，100 Hz | 1.0E-3 | IEC 60250 | |
| 23℃，1 MHz | 9.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | IEC 60112 | ||
| Solution A | 250 | V | IEC 60112 |
| Solution B | 100 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Glowing wire flammability index | 850 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.573 | ISO 489 | |
| Transmittance | |||
| 1000 µm | 89.0 | % | ISO 13468-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Electrolytic corrosion | |||
| 23℃ | A1 | IEC 60426 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2450 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 74.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 6.6 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | |||
| 23℃ | > 50 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2450 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 108 | MPa | ISO 178 |
| Ball hardness | 127 | MPa | ISO 2039-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2 mm |
| 3. 0.079 in/min |
| 4. Procedure A |
| 5. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |