APEL™ APL6013T

About
APEL™ APL6013T APEL™ APL6013T is a Cyclic Olefin Copolymer (COC) material. It is available in North America. Typical application of APEL™ APL6013T: Bottles&&APEL™ APL6013T APEL is a cyclo olefin copolymer (COC) developed by Mitsui Chemicals using Ziegler polymerization technology. Integration of the performance of polyolefin resins and that of amorphous resins enables control of heat resistance and fluidity. With the highest refractive index among amorphous polyolefins, it is low in optical anisotropy and extremely low in birefringence. Proven applications in optical plastic lenses. Excellent moisture-proof properties, chemical resistance and non-attachment characteristics that make it applicable as a medical packaging material. APEL’s versatile functions and superior characteristics create new potential for transparent materials. Features: Optical characteristics Moisture-proofness Chemical resistance Dimensional stability Heat resistant stiffness Superior moldability Applications: Industrial parts&&

About

APEL™ APL6013T APEL™ APL6013T is a Cyclic Olefin Copolymer (COC) material. It is available in North America. Typical application of APEL™ APL6013T: Bottles&&APEL™ APL6013T APEL is a cyclo olefin copolymer (COC) developed by Mitsui Chemicals using Ziegler polymerization technology. Integration of the performance of polyolefin resins and that of amorphous resins enables control of heat resistance and fluidity. With the highest refractive index among amorphous polyolefins, it is low in optical anisotropy and extremely low in birefringence. Proven applications in optical plastic lenses. Excellent moisture-proof properties, chemical resistance and non-attachment characteristics that make it applicable as a medical packaging material. APEL’s versatile functions and superior characteristics create new potential for transparent materials. Features: Optical characteristics Moisture-proofness Chemical resistance Dimensional stability Heat resistant stiffness Superior moldability Applications: Industrial parts&&

Product Description
Supplier	Mitsui
Generic	COC
Material Status	Commercial: Active
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.04	g/cm³	ASTM D792
Melt Flow Rate
260℃，2.16kg	15	g/10min	ASTM D1238
Shrinkage rate
MD	0.60	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	60.0	MPa	ASTM D638
Tensile strain
fracture	3.0	%	ASTM D638
Bending modulus	3000	MPa	ASTM D790
bending strength	110	MPa	ASTM D790

film	Nominal value	Unit	Test method
Water vapor transmittance	0.090	g·mm/m²/atm/24 hr	ASTM F1249

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	25	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	115	℃	ASTM D648
Glass transition temperature	125	℃	DSC

optical performance	Nominal value	Unit	Test method
Refractive index	1.540		ASTM D542
Transmittance	90.0	%	ASTM D1003
Haze	3.0	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.