| APICAL 300AF021是一种热固性聚酰亚胺材料,。 该产品在北美洲有供货,。 APICAL 300AF021的主要特性有: 阻燃/额定火焰 Flame Retardant 耐化学品 耐潮性 良好的密封性能 APICAL 300AF021的典型应用领域为:电影&& |
| Product Description | |
|---|---|
| Supplier | Kaneka |
| Generic | PI |
| Material Status | Commercial: Active |
| Features | Good heat sealing,Flame Characteristics,Moisture resistance,Solvent resistance,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | ASTM D1505 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 76 | µm | |
| Secant modulus | |||
| 1% secant, MD | 2790 | MPa | ASTM D882 |
| tensile strength | |||
| MD, fracture | 193 | MPa | ASTM D882 |
| Tensile strain | |||
| MD, fracture | 90 | % | ASTM D882 |
| Elmandorf tear strength | |||
| MD | 36 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance, 0.075 mm | 240 | ℃ | UL 746 |
| 0.075 mm | 210 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | |||
| 0.05 mm | 90.0 | sec | ASTM D495 |
| Compared to the resistance to leakage and marking index | |||
| 0.0500 mm | 213 | V | UL 746 |
| High Arc Burning Index (HAI) (0.0500 mm) | 22.5 | UL 746 | |
| High voltage arc marking rate (HVTR) (0.0500 mm) | 150 | mm/min | UL 746 |
| Hot wire ignition (HWI) (0.0750 mm) | 120 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.075 mm | V-0 | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |