| About |
|---|
| Product Description | |
|---|---|
| Supplier | Aramco |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | High impact resistance,Rigid-tough balance,Heat Stabilized |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| MD | 1.4 | % | SUMIKA |
| TD | 1.7 | % | SUMIKA |
| Melt Flow Rate | 24.5 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm³ | ASTM D792 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 151 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 0.45 MPa | 124 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23°C | 9 | KJ/m² | ASTM D256 |
| -20°C | 6 | KJ/m² | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 26 | MPa | ASTM D638 |
| fracture | 17 | MPa | ASTM D638 |
| Bending modulus | 1430 | MPa | ASTM D790 |
| Rockwell hardness | 91 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Processing conditions | Nominal value | Unit | Test method |
| Processing temperature | 190-230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |