| Aramco PP HP30EG是一种均聚聚丙烯树脂，通常用于双轴取向薄膜的挤出。 由这种树脂制成的薄膜通常表现出优异的光学性能，优异的机械和防潮性能。 该产品易于加工，通常适用于高速BOPP生产线。典型应用 食品包装，印刷层压，胶粘带，卷烟包装，金属化膜。 本产品不适用于医疗和制药应用。 |
| Product Description | |
|---|---|
| Supplier | Aramco |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm³ | ASTM D792 Method A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| 10N | 153 | ℃ | ASTM D1525 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.8 | kJ/m² | ASTM D256 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 155 | ASTM D2457 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| MD, fracture | 110 | MPa | ASTM D882 |
| TD, fracture | 215 | MPa | ASTM D882 |
| Tensile elongation at break | |||
| MD | 85 | % | ASTM D882 |
| TD | 15 | % | ASTM D882 |
| 1% secant modulus | |||
| MD | 2100 | MPa | ASTM D882 |
| TD | 3850 | MPa | ASTM D882 |
| Haze | 0.1 | % | ASTM D1003 |
| Tensile strain | |||
| yield | 9 | % | ASTM D638 |
| fracture | 165 | % | ASTM D638 |
| Bending modulus | 1265 | MPa | ASTM D790 |
| bending strength | 35 | MPa | ASTM D790 |
| hardness | 98 | R | ASTM D785 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |