| About |
|---|
| Aristech Quarite Select Plus® is an Acrylic material. It is available in North America for thermoforming. Important attributes of Aristech Quarite Select Plus® are: Flame Rated Low to No Odor/Taste&& |
| Product Description | |
|---|---|
| Generic | SMMA |
| Material Status | Commercial: Active |
| Features | Low odor,HB |
| Availabilitys | North America |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| Saturation, 7.11 mm | 0.19 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 7.11mm | 120 | J/m | ASTM D256-A |
| Dart impact equipped with measuring instruments | |||
| 7.11 mm | > 40.7 | J | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 7.11 mm | 87.8 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：7.11 mm | 8.1E-5 | 1/℃ | ASTM D696 |
| thermal stability | |||
| 180 ℃, 6.99 to 7.24 mm | No Effect | ASTM D4802 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 7.1 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot and Cold Cycle -50 | |||
| -29 to 82 ℃, 6.99 to 7.24 mm | No Effect | Internal Method | |
| Hot forming temperature | Internal Method | ||
| ABS side: 6.99 to 7.24 mm | 300 to 340 | Internal Method | |
| Acrylic side: 6.99 to 7.24 mm | 177 to 193 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-grade, 7.11 mm | 90 to 100 | ASTM D785 | |
| Babbitt hardness | |||
| 7.11 mm | 48 to 52 | ASTM D2583 | |
| Tensile modulus | |||
| 7.11 mm | 2620 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 7.11 mm | 39.3 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 7.11 mm | 3.5 | % | ASTM D638 |
| Bending modulus | |||
| 7.11 mm | 2230 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| 7.11 mm | 70.3 | MPa | ASTM D790 |
| 7.11 mm | 81.4 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.275 to 0.285 in |
| 3. 0.275 to 0.285 in, Acrylic in Tension |
| 4. 0.275 to 0.285 in, Acrylic in Compression |
| 5. 0.275 to 0.285 in, FTMS 406 M-1074 |
| 6. 30 min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |