| About |
|---|
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | PA 6T |
| Material Status | Commercial: Negative |
| Features | Flame Characteristics,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.72 | g/cm³ | ASTM D792 |
| Molding shrinkage | |||
| TD：2.0 mm | 0.80 | % | ASTM D955 |
| MD：2.0 mm | 0.40 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| 100℃，24hr | 3.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | 70 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 295 | ℃ | ASTM D648 |
| Glass Transition Temperature | 85.0 | ℃ | DSC |
| Melting temperature | 310 | ℃ | |
| Coeff. of linear thermal expansion | |||
| TD | 5.0E-5 | 1/℃ | ASTM D696 |
| MD | 2.4E-5 | 1/℃ | ASTM D696 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 1 MHz | 3.90 | ASTM D150 | |
| Dissipation Factor | |||
| 1 MHz | 0.012 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 170 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK | 3.0 | % | ASTM D638 |
| Flexural Modulus | 12000 | MPa | ASTM D790 |
| Flexural Strength | 260 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 110 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 110 | °C | null |
| Drying Time | 2.0 to 6.0 | hr | null |
| Hopper Temperature | 50 to 90 | °C | null |
| Rear Temperature Zone 1 | 300 to 325 | °C | null |
| Middle Temperature Zone 2 | 315 to 335 | °C | null |
| Front Temperature Zone 3 | 320 to 335 | °C | null |
| Nozzle temperature | 315 to 335 | °C | null |
| Mold Temperature | 90 to 140 | °C | null |
| Injection speed | Moderate | null | |
| Screw Speed | 150 | rpm | null |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |