ARLEN™ E630N

About
ARLEN™ E630N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ E630N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating. Features: High dimensional stability High melting point High rigidity Minimum water absorption Good chemical and heat resistance Flame retardant Applications: Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.&&

About

ARLEN™ E630N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ E630N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating. Features: High dimensional stability High melting point High rigidity Minimum water absorption Good chemical and heat resistance Flame retardant Applications: Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.&&

Product Description
Supplier	Mitsui
Generic	PA 6T
Material Status	Commercial: Negative
Features	Good stability,Low or no water absorption,Heat Resistance, Good,Flame Characteristics,Good Rigidity,Solvent resistance,V-0
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.58	g/cm³	ASTM D792
Molding shrinkage			ASTM D955
MD	0.20	%	ASTM D955
TD	0.80	%	ASTM D955
Water Absorption
23℃，24hr，65% RH	2.1	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Izod Notched Impact strength	100	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature HDT
1.8 MPa, unannealed	310	℃	ASTM D648
Glass Transition Temperature	95.0	℃
Melting temperature	320	℃
Coeff. of linear thermal expansion			ASTM E831
MD	1.6E-5	1/℃	ASTM E831
TD	6.8E-5	1/℃	ASTM E831

ELECTRICAL	Nominal value	Unit	Test method
Volume Resistance	1.0E+15	ohms·cm	ASTM D257
Dielectric Strength	24	kV/mm	ASTM D149
Dielectric Constant
1 MHz	3.90		ASTM D150
Dissipation Factor
1 MHz	0.013		ASTM D150

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame Class Rating	V-0		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
M-level	100		ASTM D785
Tensile Strength	210	MPa	ASTM D638
Tensile Strain
Broken BRK	6.0	%	ASTM D638
Flexural Modulus	12500	MPa	ASTM D790
Flexural Strength	275	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.