| Arlon® 1263 is a Polyetheretherketone (PEEK) product filled with carbon fiber. It can be processed by injection molding and is available in Europe or North America. Typical application: Military Applications.&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Active |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ASTM D792 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 316 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | ASTM D696 | ||
| < 149℃ | 1.3E-5 | cm/cm/℃ | ASTM D696 |
| > 149℃ | 3.1E-5 | cm/cm/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 92 | ASTM D2240 | |
| Rockwell hardness | |||
| M-level | 108 | ASTM D785 | |
| Tensile modulus | |||
| 0.5% 割线 | 21700 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 230 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.9 | % | ASTM D638 |
| Bending modulus | |||
| 0.5% secant | 19000 | MPa | ASTM D790 |
| bending strength | 347 | MPa | ASTM D790 |
| compressive strength | 262 | MPa | ASTM D695 |
| shear strength | ASTM D732 | ||
| — | 120 | MPa | ASTM D732 |
| — | 95.8 | MPa | ASTM D732 |
| friction coefficient | |||
| With oneself – dynamic | 0.18 | ASTM G77 | |
| Load deformation | 0.0600 | % | ASTM D621 |
| Wear factor | 460 | 10^-8 mm³/N·m | ASTM G77 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. at Break |
| 3. Transverse |
| 4. Axial |
| 5. PV = 12600 psi-ft/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |