| About |
|---|
| Arnite® AV2 370 /B是一种聚对苯二甲酸乙二酯(PET)材料,含有的填充物为35% 玻璃纤维增强材料。 该产品在欧洲或亚太地区有供货,加工方式为:注射成型。 Arnite® AV2 370 /B的主要特性有: 阻燃/额定火焰 脱模剂 典型应用领域包括: 汽车行业 工程/工业配件&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 0.45 | % | ISO 62 |
| 23℃，50% RH | 0.18 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 185 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 12620 | MPa | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 235 | ℃ | ISO 75-2/Af |
| Melting temperature | 255 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | |||
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-5 | 1/℃ | ISO 11359-2 |
| TD | 2.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | >1.0E+15 | Ω.cm | IEC 60093 |
| Insulation strength | 0.840 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 3.50 | IEC 60250 | |
| 100 Hz | 3.70 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 3.0E-3 | IEC 60250 | |
| 100 Hz | 0.013 | IEC 60250 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 69.3 | kJ/m² | ISO 179/1eU |
| -30℃ | 50.4 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 9.5 | kJ/m² | ISO 179/1eA |
| -30℃ | 9.5 | kJ/m² | ISO 179/1eA |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 -120 | °C | |
| Drying time | 3.0-12 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 270-280 | °C | |
| Central temperature of the barrel | 270-290 | °C | |
| Barrel front temperature | 270-290 | °C | |
| Die temperature | 270-290 | °C | |
| Mold temperature | 130-140 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |