| About |
|---|
| 57 Shore D, Extrusion, Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | TPC-ES |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 17.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.11 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 4.8 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 5.4 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 71.0 | ℃ | ISO 306 |
| Melting temperature | 205 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 100 Hz | 4.20 | ||
| 1 MHz | 3.50 | ||
| Dissipation factor | |||
| 100 Hz | 0.018 | ||
| 1 MHz | 0.050 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 98 | ||
| Shore A, 15 seconds | 97 | ||
| Shore D, 3 seconds | 57 | ||
| Shore D, 15 seconds | 57 | ||
| Tensile modulus | 205 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 27.0 | MPa | |
| 5% strain | 9.70 | MPa | |
| 10% strain | 14.0 | MPa | |
| 50% strain | 18.0 | MPa | |
| 100% strain | 17.0 | MPa | |
| Nominal tensile fracture strain | 430 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |