| About |
|---|
| 50% Renewable Content&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 45.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.040 | % | ISO 62 |
| Biomass content | 52 | % | ASTM D6866 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 90.0 | ℃ | ISO 306/A50 |
| Melting temperature | 158 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 20 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.5 mm | HB | IEC 60695-11-10, -20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 34 | ISO 868 | |
| Tensile modulus | 50.0 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 12.0 | MPa | |
| 5% strain | 2.70 | MPa | |
| 10% strain | 4.50 | MPa | |
| 50% strain | 7.70 | MPa | |
| 100% strain | 8.30 | MPa | |
| Nominal tensile fracture strain | 300 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |