| About |
|---|
| Injection Molding or Extrusion Grade, Drinking Water Grade&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Apparent density | 0.69 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 33.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.5 | % | ISO 294-4 |
| MD | 1.5 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.75 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 33 | ISO 868 | |
| Tensile modulus | 40.0 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| fracture | 21.0 | MPa | ISO 527-2 |
| 5% strain | 2.10 | MPa | ISO 527-2 |
| 10% strain | 3.50 | MPa | ISO 527-2 |
| 50% strain | 6.50 | MPa | ISO 527-2 |
| 100% strain | 7.30 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | 830 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | No Break | ISO 179/1eA | |
| 23℃ | No Break | ISO 179/1eA | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | No Break | ISO 180/1A | |
| 23℃ | No Break | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 195 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 2.2E-4 | 1/℃ | ISO 11359-2 |
| MD | 2.2E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 20 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 4.10 | IEC 60250 | |
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.017 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 190 to 210 | °C | |
| Barrel middle temperature | 200 to 220 | °C | |
| Barrel front temperature | 210 to 230 | °C | |
| Nozzle temperature | 220 to 240 | °C | |
| Processing (melt) temperature | 220 to 240 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Melt temperature | 205 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |