| About |
|---|
| Flame Retardant (halogen- phosphorous-free)&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | TPC-ES |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Low to no phosphorus content,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 14 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 15.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.60 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore D, 3 seconds | 55 | ISO 868 | |
| Shore D, 15 seconds | 55 | ISO 868 | |
| Tensile modulus | 250 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| fracture | 27.0 | MPa | ISO 527-2 |
| 10% strain | 13.0 | MPa | ISO 527-2 |
| 100% strain | 17.5 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | 380 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | No Break | ISO 179/1eA | |
| Impact strength of cantilever beam notch | |||
| 23℃ | No Break | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 85.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 90.0 | ℃ | ISO 306 |
| Melting temperature | 200 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 20 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 100 Hz | 5.20 | IEC 60250 | |
| Dissipation factor | |||
| 100 Hz | 2.0E-6 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.5 mm | V-2 | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 210 to 230 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Nozzle temperature | 230 to 250 | °C | |
| Processing (melt) temperature | 230 to 250 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |