| About |
|---|
| Polyaryletherketone with Tg of 446°F (230°C)&& |
| Product Description | |
|---|---|
| Generic | PAEK |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3000 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 98.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 | % | ASTM D638 |
| Bending modulus | 3000 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 230 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 180 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 380 | °C | |
| Barrel middle temperature | 380 | °C | |
| Barrel front temperature | 380 | °C | |
| Nozzle temperature | 380 | °C | |
| Mold temperature | 200 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |