| About |
|---|
| 黑色通用级 |
| Product Description | |
|---|---|
| Supplier | German |
| Generic | ASA |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| 50 mm/min | 45 | MPa | ASTM D638 |
| Elongation at break | |||
| 50mm/min | 30 | % | ASTM D638 |
| bending strength | |||
| 2 mm/min | 60 | MPa | ASTM D790 |
| Bending modulus | |||
| 2 mm/mim | 2100 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 85 | ℃ |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt index | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | 0.4-0.7 | % | ASTM D955 |
| Flame retardant level | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | KJ/m² | ISO180-A |
| Process Conditions | |||
|---|---|---|---|
| Processing performance | Nominal value | Unit | Test method |
| Processing temperature range | 200-210 | ˚C | |
| Optimal processing temperature | 205 | ˚C | |
| Mold temperature | 50-80 | ˚C | |
| Drying temperature | 85 | ˚C | |
| Drying time | 3-4 | h | |
| Moisture content | ≤0.04 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |