| About |
|---|
| Injection & extrusion molding grade. For molded products with superior rigidity, and good surface appearance. It is supplied in pellet form. Containers, stationery goods, toys, and consumer goods.&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | SBS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Copolymer |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.0 | g/10min | ISO 1133 |
| Shrinkage rate | 0.20 to 0.80 | % | |
| Water absorption rate | |||
| 23℃，24hr | < 0.10 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| Complete fracture | 1.1 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| Complete fracture | 23 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 69.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 96.0 | ℃ | ISO 306/A50 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2000 µm | 90.0 | % | ISO 13468 |
| Haze | |||
| 2000 µm | 3.0 | % | ISO 14782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 75 | ISO 868 | |
| Rockwell hardness | |||
| R-level | 78 | ISO 2039-2 | |
| tensile strength | |||
| yield | 41.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 12 | % | ISO 527-2/5 |
| Bending modulus | 2250 | MPa | ISO 178 |
| bending strength | 54.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |