| About |
|---|
| PP 3495 is a high flow, high impact copolymer polypropylene suitable for injection molding applications specified by Toyota TSM 5514G-3A, and which require a material with the following properties.&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Impact copolymer |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.898 | g/cm³ | |
| Melt Flow Rate | |||
| 230℃，2.16kg | 30 | g/10min | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 150 | J/m | |
| Notched impact strength of cantilever beam | |||
| -30℃ | No Break |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 98 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 21.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ℃ | 6.0 | % | |
| Bending modulus | |||
| 23℃ | 1000 | MPa | |
| bending strength | |||
| 23℃ | 25.0 | MPa | |
| Rockwell hardness | |||
| R-level | 71 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 500 J/m |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |